Idumah CI, Nwachukwu AN and Akubue B
Poly (lactic acid) (PLA) is an aliphatic polyester and ecofriendly material of a natural origin with biodegradable properties. The monomer for PLA is lactic acid obtained from the fermentation of sugar and vegetables like corn and cassava. This study investigated the effect of heatsetting and wet processes on the tensile properties of treated and untreated Ingeo™ Poly (Lactic acid) PLA knitted fabrics. PLA samples of dimension 200 mm×200 mm were subjected to heatsetting at a temperature of 130°C and increasing times of 15s, 30s, 45s, 60s, 90s, 120s and 240s respectively using the Werner Mathis infra red heatsetting equipment and subsequently treated to wet processes including scouring, alkaline reduction clearing, dyeing and softening. Four tensile parameters were determined in warp and weft direction using the KES-FB system of fabric evaluation. These tensile parameters were tensile extension EM [%], linearity of load extension LT [-], tensile energy WT [g.cm/cm2] and tensile resilience RT [%]. Results indicated a remarkable change in tensile properties of PLA with increasing times of heat setting and wet processes.
PDFShare this article
Journal of Textile Science & Engineering received 1008 citations as per Google Scholar report